STAINLESS STEEL RODS are a type of stainless steel product that is in a cylindrical shape and made up of stainless steel grades- 304, 321, and 316 most commonly. These stainless steel round bars are usually used in sectors like the food industry or construction businesses.Stainless steel is an alloy of iron that is resistant to rusting and corrosion. It contains at least 11% chromium and may contain elements such as carbon, other nonmetals and metals to obtain other desired properties.
| Specifications | ASTM B446 / ASTM SB446 |
| size | 2-100mm A/F |
|---|---|
| Square bar size | 4 to 100mm |
| Flat bar size | Thickness: 2 -100mm Width: 10 to 500mm |
| Round bar size | Diameter: 3-~800mm |
| Rectangles Size | 33 x 30mm to 295 x 1066mm |
| Angle bar size | 3mm*20mm*20mm~12mm*100mm*100mm |
| Section | 3.0 to 12.0mm thickness |
| Hollow Bar | 32mm OD x 16mm ID to 250mm OD x 200mm ID) |
| Finish | Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black |
| Technique | Cold Drawn, Hot Rolled, Forged Round Bar,Cold Rolled, Rod |
| Metric | US Bar | ASTM/ Canadian | Japanese | ||||
|---|---|---|---|---|---|---|---|
| Bar Size | Diam. (mm) | Bar Size | Diam. (Inch) | Bar Size | Diam. (mm2) | Bar Size | Diam. (mm) |
| 5 | 5 | #2 | 0.250 | 10M | 100 | 6 | 6 |
| 5.5 | 5.5 | #3 | 0.375 | 15M | 200 | 10 | 10 |
| 6 | 6 | #4 | 0.500 | 20M | 300 | 13 | 13 |
| 7 | 7 | #5 | 0.600 | 25M | 500 | 16 | 16 |
| 8 | 8 | #6 | 0.750 | 30M | 700 | 19 | 19 |
| 9 | 9 | #7 | 0.875 | 35M | 1000 | 22 | 22 |
| 10 | 10 | #8 | 1.000 | 45M | 1500 | 25 | 25 |
| 11 | 11 | #9 | 1.125 | 55M | 2500 | 29 | 29 |
| 12 | 12 | #10 | 1.250 | 32 | 32 | ||
| 14 | 14 | #11 | 1.375 | 35 | 35 | ||
| 16 | 16 | #12 | 1.500 | 38 | 38 | ||
| 18 | 18 | #13 | 1.600 | 41 | 41 | ||
| 20 | 20 | #14 | 1.750 | 44 | 44 | ||
| 22 | 22 | #15 | 1.875 | 48 | 48 | ||
| 25 | 25 | #16 | 2.000 | 51 | 51 | ||
| 28 | 28 | #18 | 2.250 | 57 | 57 | ||
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 304 | min. | – | – | – | – | – | 18.0 | – | 8.0 | – |
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 304 | 515 | 205 | 40 | 92 | 201 |