Stainless Steel Buttweld Fittings Available in wide varieties, ranging from small to large diameters, these pipe fittings are offered with maximum pressure rating.Stainless Steel Buttweld Pipe Fittings, which offers faster machining speeds, longer tool life, improved part quality and lower total cost of machined parts.
| Dimensions | ASME/ANSI B16.9, ASME B16.28, MSS-SP-43 |
| Sizes | 1/2″NB TO 48″NB IN |
| Types | Welded Fittings, Buttweld Welded Fittings |
| Wall Thickness | Schedule 5S, 10S, 20S, S10, S20, S30, STD, 40S, S40, S60, XS, 80S, S80, S100, S120, S140, S160, XXS and etc. |
| Value Added Services | Hot Dipped Galvanizing, Epoxy & FBE Coating, Electro Polish, Sand Blasting, Threading, Soldering |
| Production Grades | Stainless Steel, Alloy Steel, Duplex, Nickel Alloys, Low temperature Steel, Carbon Steel, Cupro Nickel |
| Grade | C | Mn | Si | P | S | Cr | Ni |
|---|---|---|---|---|---|---|---|
| SS 304 | 0.08 max | 2 max | 0.75 max | 0.045 max | 0.030 max | 18 – 20 | 8 – 11 |
| Grade | C | Mn | Si | P | S | Cr | Ni |
|---|---|---|---|---|---|---|---|
| SS 304L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.03 max | 18 – 20 | 8 – 13 |
| Grade | C | Mn | P | Si | Ni | Fe | S | Cr | Mo |
|---|---|---|---|---|---|---|---|---|---|
| SS 316L | 0.035 max | 2.0 max | 0.045 max | 1.0 max | 10.00 – 14.00 | 68.89 min | 0.030 max | 16.00 – 18.00 | 2.00 – 3.00 |
| SS 316 | 0.08 max | 2.0 max | 0.045 max | 1.0 max | 11.00 – 14.00 | 67.845 min | 0.030 max | 16.00 – 18.00 | 2.00 – 3.00 |
| Grade | C | Mn | P | S | Si | Cr | Ni | Mo | Fe |
|---|---|---|---|---|---|---|---|---|---|
| SS 316Ti | 0.08 max | 2.0 max | 0.045 max | 0.030 max | 0.75 max | 16.00 – 18.00 | 10.00 – 14.00 | 2.00 – 3.00 | 68.395 min |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
|---|---|---|---|---|---|
| 304 | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
|---|---|---|---|---|---|
| 304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
| Grade | Melting Point | Density | Elongation | Tensile Strength | Yield Strength (0.2%Offset) |
|---|---|---|---|---|---|
| SS 316L | 1399 °C (2550 °F) | 8.0 g/cm3 | 35 % | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 |
| SS 316 | 1400 °C (2550 °F) | 8.0 g/cm3 | 35 % | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 |
| Grade | Density | Tensile Strength | Melting Point | Yield Strength (0.2%Offset) | Elongation |
|---|---|---|---|---|---|
| 316Ti | 8.0 g/cm3 | Psi – 75000 , MPa – 515 | 1399 °C (2550 °F) | Psi – 30000 , MPa – 205 | 35 % |